Lembaran Keluli Tahan Karat 201 untuk pelanggan
Mar 16, 2026
Tinggalkan pesanan
| Standard | ASTM A240, EN 10088-2, GB/T 3280 |
|---|---|
| Gred | 1.4372, SUS201, X12CrMnNiN17-7-5, Z12CMN17-07Az |
| Panjang | 2000 mm-6000 mm (78.74-236.22 in), Disesuaikan |
| Lebar Penuh | 1000 mm-2000 mm (39.37-78.74 in), Disesuaikan |
| Ketebalan | 0.3 mm-6 mm (0.012-0.24 in), Disesuaikan |
| Kemasan Permukaan | 2B, 8K, BA, dsb., HL, No.1, No.4 |
| Teknik | Ditarik Sejuk, Digulung Sejuk, Digulung Panas |
| Borang | Gegelung, Cadar Canai Sejuk, Cadar Timbul, dsb., Plat & Cadar Rata, Cadar Canai Panas, Cadar Berlubang, Plat, Cadar Bergilap, Jalur, Cadar Bertekstur |
Komposisi Kimia
| unsur | Karbon (C) | Mangan (Mn) | Silikon (Si) | Fosforus (P) | Sulfur (S) | Chromium (Cr) | Nikel (Ni) | Nitrogen (N) |
|---|
| Komposisi (%) | 0.15 maks | 5.5-7.5 | 1.0 maks | 0.06 maks | 0.03 maks | 16.0-18.0 | 3.5-5.5 | 0.25 maks |
Sifat Mekanikal
| Hartanah | Unit Metrik | Unit Imperial |
|---|
| Kekuatan Tegangan | 655 – 860 MPa | 95 – 125 ksi |
| Kekuatan Hasil | 450 MPa | 65 ksi |
| Kekerasan Vickers | 230 – 270 HV | 230 – 270 HV |
| Kekerasan Brinell | 200 – 250 HB | 200 – 250 HB |
| Kekerasan Rockwell | 50 – 56 HRC | 50 – 56 HRC |
| Pemanjangan | 20% | 20% |
| Modulus Elastik | 200 GPa | 29 x 10^6 psi |