🧪 Komposisi Kimia
| unsur | Komposisi (%) |
|---|---|
| Karbon (C) | ≤ 0.15 |
| Mangan (Mn) | ≤ 1.00 |
| Silikon (Si) | ≤ 1.00 |
| Fosforus (P) | ≤ 0.040 |
| Sulfur (S) | ≤ 0.030 |
| Chromium (Cr) | 11.5 - 13.5 |
| Nikel (Ni) | ≤ 0.75 |
| Besi (Fe) | Baki |
⚙️ Sifat Mekanikal
| Harta benda | Keadaan Annealed | Mengeras & Marah |
|---|---|---|
| Kekuatan Tegangan | 485-620 MPa | 725-850 MPa |
| Kekuatan Hasil (0.2% offset) | 275-415 MPa | 550-690 MPa |
| Pemanjangan (50mm) | ≥ 20% | ≥ 15% |
| Pengurangan Kawasan | ≥ 50% | ≥ 45% |
| Kekerasan (Brinell) | 155-217 HB | 235-285 HB |
| Kekerasan (Rockwell C) | - | 22-32 HRC |
| Tenaga Kesan (Charpy V-takik) | 54-81 J | 27-54 J |
| Had Keletihan (10&sup7; kitaran) | 240 MPa | 360 MPa |
🔬 Sifat Fizikal
| Harta benda | Nilai |
|---|---|
| Ketumpatan | 7.75 g/cm³ |
| Takat Lebur | 1480-1530°C |
| Haba Tentu (20°C) | 460 J/kg·K |
| Kekonduksian Terma (100°C) | 24.9 W/m·K |
| Pengembangan Terma (20-100°C) | 9.9×10-6/K |
| Pengembangan Terma (20-500°C) | 11.2×10-6/K |
| Kerintangan Elektrik (20°C) | 0.57 µΩ·m |
| Kebolehtelapan Magnet | Ferromagnetik |
| Modulus Keanjalan | 200 GPa |
| Nisbah Poisson | 0.27-0.30 |
📏 Spesifikasi Produk
| Borang Produk | Julat Saiz | Piawaian |
|---|---|---|
| Bar Bulat | diameter 6-300mm | ASTM A276, A479 |
| Bar Segiempat | 10-150mm | ASTM A276 |
| Bar Rata | 3-100mm tebal, sehingga 300mm lebar | ASTM A276 |
| cadar | 0.5-6mm tebal, sehingga 2000mm lebar | ASTM A240 |
| Pinggan | 6-100mm tebal, sehingga 3000mm lebar | ASTM A240 |
| tiub | 6-219mm OD, dinding 0.5-20mm | ASTM A268 |
| Kemasan Permukaan | Digulung panas, ditarik sejuk, digilap | 2B, BA, No.4, No.8 |
| Toleransi | ±0.1mm hingga ±1.0mm | EN 10029, ASTM A480 |