Apakah Keluli Tahan Karat 201?
Mar 23, 2026
Tinggalkan pesanan
Standard dan Gred Setara
| ASTM | JIS | UNS | EN | DIN | GOST | GB |
|---|---|---|---|---|---|---|
201 | SUS201 | S20100 | 1.4372 | X12CrMnNiN17-7-5 | 12Х15Г9НД | 12Cr17Mn6Ni5N |
Komposisi Kimia 201 Tahan Karat
| Gred | Standard | C | Cr | Ni | Mn | Si | P | S | Mo | Fe |
|---|---|---|---|---|---|---|---|---|---|---|
201 | ASTM A240 | ≤0.15 | 16.0–18.0 | 3.5–5.5 | 5.5–7.5 | ≤1.0 | ≤0.06 | ≤0.03 | – | Baki |
1.4372 | EN 10088-2 | ≤0.15 | 16.0–18.0 | 3.5–5.5 | 5.5–7.5 | ≤1.0 | ≤0.06 | ≤0.03 | – | Baki |
SUS201 | JIS G 4304 | ≤0.15 | 16.0–18.0 | 3.5–5.5 | 5.5–7.5 | ≤1.0 | ≤0.06 | ≤0.03 | – | Baki |
Berbanding dengan 304, nikel dikurangkan manakala mangan meningkat, yang mengurangkan kos tetapi mengehadkan rintangan kakisan dalam persekitaran yang agresif.
Sifat Mekanikal
| Gred | Standard | Kekuatan Tegangan | Kekuatan Hasil | Pemanjangan | Kekerasan |
|---|---|---|---|---|---|
201 | ASTM A240 | ≥ 520 MPa | ≥ 275 MPa | ≥ 40% | ≤ 95 HBW |
1.4372 | EN 10088-2 | ≥ 520 MPa | ≥ 275 MPa | ≥ 40% | ≤ 95 HBW |
SUS201 | JIS G 4304 | ≥ 520 MPa | ≥ 275 MPa | ≥ 40% | ≤ 95 HBW |
Varian Keluli Tahan Karat 201: J1, J2, J4
Untuk membantu anda memilih dengan lebih baik, berikut ialah cara J1, J2 dan J4 berbeza:
| Varian | Pelarasan Komposisi Biasa | Ciri-ciri | Kegunaan Biasa |
|---|---|---|---|
201 J1 | Ni ~4.0–4.5%, Cu ~1.5% | Kebolehbentukan dan keupayaan regangan yang sangat baik | Peralatan dapur, singki, alat memasak |
201 J2 | Tinggi sedikit C, rendah Cu | Kekuatan yang lebih tinggi, kurang pemanjangan | pemanjangan Pengikat, profil perindustrian, pembinaan |
201 J4 | Ni rendah (~3.5%), Mn lebih tinggi, Cu ~1.5% | Terbaik untuk kemasan hiasan, kos yang lebih rendah | Pintu, panel, hiasan dalaman |